Título: Mechanical properties of sintered La9.33Si2Ge4O26 oxyapatite materials for SOFC electrolytes
Autor: Santos, Miguel
Alves, Cátia
Oliveira, F. A. Costa
Marcelo, Teresa
Mascarenhas, João
Fernandes, J.V.
Trindade, B.
Palavras-chave: C. Mechanical properties
Lanthanum-based oxyapatite
Mechanical alloying
SOFC
Data: 2012
Editora: Elsevier
Citação: Santos, M.; Alves, C.; Oliveira, F.A.C.; Marcelo, T.; Mascarenhas, J.; Fernandes, J.V.; Trindade, B. Mechanical properties of sintered La9.33Si2Ge4O26 oxyapatite materials for SOFC electrolytes. In: Ceramics International, 2012, vol. 38, nº 8, p. 6151-6156
Resumo: Mechanical properties of La9.33Si2Ge4O26 prepared by mechanical alloying and subsequent sintering at 1300–1400 °C for 1 h were evaluated. Hardness and Young's modulus values in the range 7.3–9.6 GPa and 106–135 GPa, respectively, were obtained from nanohardness tests. The fracture toughness values derived from the Palmqvist method varied between 3.5 and 3.9 MPa m1/2 from classical microindentation test with an indentation load of 9.8 N. Yield stress (σy) was determined by inverse analysis from microhardness tests. The maximum value of σy (1829 MPa) was obtained for the sample sintered at 1400 °C showing the highest density (5.42 g/cm3).
URI: http://hdl.handle.net/10400.9/1693
ISSN: 0272-8842
Versão do Editor: http://dx.doi.org/10.1016/j.ceramint.2012.04.065
Aparece nas colecções:UEP - Artigos em revistas internacionais

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
FOliveira_CeramicsInternational.pdf131,02 kBAdobe PDFVer/Abrir


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.