Título: Oxide loading effect on the electrochemical performance of LaNiO3 coatings in alkaline media
Autor: Soares, C. O.
Silva, R. A.
Carvalho, M. D.
Jorge, M. E. Melo
Gomes, A.
Rangel, C. M.
Palavras-chave: LaNiO3 films
Nickel-foam support 
Roughness
Cyclic voltammetry
Electrochemical impedance spectroscopy
Data: 2013
Editora: Elsevier
Citação: Soares, C.O.; Silva, R.A.; Carvalho, M.D.; Jorge, M.E. Melo; Gomes, A.; Rangel, C.M. Oxide loading effect on the electrochemical performance of LaNiO3 coatings in alkaline media. In: Electrochimica Acta, 2013, Vol. 89, p. 106-113
Resumo: LaNiO3 film electrodes were prepared by brush painting using nickel-foam supports in order to increase its surface area available for electrochemical reactions. Loadings varying between 20 and 140 mg cm-2 were tested. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) were used to evaluate the coatings roughness (Rf) and morphology (f) factors, complemented by optical microscopy observations. The values obtained from the two methods are in excellent agreement. The Rf values, ranging from 848 ± 50 to 4260 ± 60, are within the highest in the open literature. A simulation, of the effect of the oxide loading on the coatings Rf values, was performed using just the experimental values of the roughness factors for oxide free foam and pelleted electrodes. It was found that the increase of oxide loading causes a quasi linear increase of the electrodes active surface area. Simulated values were in excellent agreement with the experimental roughness factors and pore resistances obtained by CV and EIS. The electrodes were tested for oxygen evolution.
URI: http://hdl.handle.net/10400.9/1991
ISSN: 0013-4686
Versão do Editor: http://dx.doi.org/10.1016/j.electacta.2012.11.040
Aparece nas colecções:UTCAE - Artigos em revistas internacionais

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
ElectrochimicaActa_CRangel.pdf189,61 kBAdobe PDFVer/Abrir


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.