|Título:||Gold deposition from 1-butyl-1-methyl-pyrrolidinium dicyanamide ionic liquid at open-circuit and under potentiostatic control|
|Autor:||Sá, A. I. Correia de|
Rangel, C. M.
|Citação:||Sá, A.I. Correia de; Eugénio, S.; Quaresma, S.; Rangel, C.M.; Vilar, R. Gold deposition from 1-butyl-1-methyl-pyrrolidinium dicyanamide ionic liquid at open-circuit and under potentiostatic control. In: Surface and Coatings Technology, 2013, Vol. 232, p. 645-651|
|Resumo:||In this work, the deposition of gold on copper substrates from solutions of HAuCl4.3H2O in 1-butyl-1-methylpyrrolidinium dicyanamide was studied. Deposition was carried out in open-circuit and under potentiostatic control at temperatures from 293 to 353 K, in normal atmosphere, with deposition conditions allowing water from atmospheric absorption up to 0.8 wt.%. Films of gold were obtained by both methods. Deposition at open-circuit occurs by galvanic displacement mechanism. Involvement of Cu+ species in the electrodeposition process was suggested by cyclic voltammetry. Furthermore, copper incorporation in the gold films was confirmed by X-ray diffraction. SEM observation and XRD analysis show that films are nanocrystalline with a globular morphology except for the films formed under potentiostatic control at 353 K, which show a dendritic structure. The size of the crystallites determined by Scherrer's equation varies in the range from 6 to 25 nm.|
|Versão do Editor:||http://dx.doi.org/10.1016/j.surfcoat.2013.06.061|
|Aparece nas colecções:||UTCAE - Artigos em revistas internacionais|
Ficheiros deste registo:
|Susface&CoatingsTechnology_CRangel.pdf||206,71 kB||Adobe PDF||Ver/Abrir|
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.