Título: Novel two-step processing route combining mechanical alloying and microwave hybrid sintering to fabricate dense La9.33Si2Ge4O26 for SOFCs
Autor: Santos, Mário João dos
Alves, Cátia
Oliveira, F. A. Costa
Marcelo, Teresa
Mascarenhas, João
Cavaleiro, A.
Trindade, B.
Palavras-chave: SOFC
Lanthanum-based oxyapatite
Mechanical Alloying
Microwave hybrid sintering
Mechanical Properties
Data: 2013
Editora: Elsevier
Citação: Santos, M.; Alves, C.; Oliveira, F.A.C.; Marcelo, T.; Mascarenhas, J.; Cavaleiro, A.; Trindade, B. Novel two-step processing route combining mechanical alloying and microwave hybrid sintering to fabricate dense La9.33Si2Ge4O26 for SOFCs. In: Journal of Power Sources, 2013, Vol. 231, p. 146-152
Resumo: In this work, microwave hybrid sintering at 1300 and 1350 °C was carried out for densification of La9.33Si2Ge4O26 mechanically alloyed powder with apatite structure. The pellets sintered at these two temperatures present the same structure (apatite) with relative densities of 92 and 96%, respectively. Mechanical analysis performed on sintered materials revealed the following results: hardness of 7.1 and 8.0 GPa, Young's modulus of 122 and 133 GPa, yield strength of 1807 and 2073 MPa and fracture toughness of 1.5 and 1.0 MPa m1/2, respectively.
URI: http://hdl.handle.net/10400.9/2093
ISSN: 0378-7753
Versão do Editor: http://dx.doi.org/10.1016/j.jpowsour.2012.12.101
Aparece nas colecções:ES - Artigos em revistas internacionais

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
JPowerSources_TMarcelo.pdf181,19 kBAdobe PDFVer/Abrir


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.