Título: Electrochemical characterization of poly(ethylene oxide)- zinc chloride system and its application in rechargeable batteries
Autor: Plancha, Maria João
Rangel, C. M.
Sequeira, C.A.C.
Data: 2008
Citação: Plancha M. J.; Rangel, C. M.; Sequeira, C. A. C. Electrochemical characterization of poly(ethylene oxide)- zinc chloride system and its application in rechargeable batteries. In: Book of Abstracts, 11th International Symposium on Polymer Electrolytes, Ofir, Portugal, 2008, p.154
Resumo: The system PEOnZnCl2 with n=4-16 was studied in view of its potential application in a solid state rechargeable zinc battery. A.c. conductivity and cationic transference number measurements, in the temperature range 20-150ºC, were performed and the electrochemical stability window was established for the polymer electrolyte with n=4 composition. The ionic conductivity, σ, of this film, follows a VTF behaviour, with an activation energy of 3.3 ± 0.2 kJ mol-1 and σ values were found between 2.50x10-7 S cm-1 at 24ºC and 4.81x10-4 S cm-1 at 145ºC. Acceptable zinc ion transference numbers of 0.36 (medium value) and decomposition voltage values between 3.19V (20ºC) and 1.44V (150ºC) were estimated. Cyclic voltammetric studies using Zn/PEO4ZnCl2/Zn cell indicated reversibility of the Zn/Zn2+ couple at the electrode/electrolyte interface. Several cells Zn(-)/PEO4ZnCl2/Nb2O5(+) were assembled and studied at 55ºC, with several discharge current densities. Results of cell’s discharge profiles, capacity values, charge-discharge cycles behaviour and stability are reported.
URI: http://hdl.handle.net/10400.9/761
Aparece nas colecções:UPCH - Resumos em livros de actas

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
ELECTROCHEMICPLANNCHA.pdf86,15 kBAdobe PDFVer/Abrir


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.