Loading...
7 results
Search Results
Now showing 1 - 7 of 7
- Consolidation of W–Ta composites: hot isostatic pressing and spark and pulse plasma sinteringPublication . Dias, Marta; Guerreiro, F.; Correia, J.B.; Galatanu, Andrei; Rosinski, M.; Monge, M. A.; Munoz, A.; Alves, E.; Almeida Carvalho, PatriciaComposites consisting of tantalum fiber/powder dispersed in a nanostructured W matrix have been consolidated by spark and pulse plasma sintering as well as by hot isostatic pressing. The microstructural observations revealed that the tungsten–tantalum fiber composites consolidated by hot isostatic pressing and pulse plasma sintering presented a continuous layer of Ta2O5 phase at the W/Ta interfaces, while the samples consolidated by spark plasma sintering evidenced a Ta + Ta2O5 eutectic mixture due to the higher temperature of this consolidation process. Similar results have been obtained for the tungsten–tantalum powder composites. A (W, Ta) solid solution was detected around the prior nanostructured W particles in tungsten–tantalum powder composites consolidated by spark and pulse plasma sintering. Higher densifications were obtained for composites consolidated by hot isostatic pressing and pulse plasma sintering.
- Blistering of W–Ta composites at different irradiation energiesPublication . Mateus, R.; Dias, Marta; Lopes, J.; Rocha, J.; Catarino, N.; Duarte, P.; Gomes, R. B.; Silva, C.; Fernandes, H.; Livramento, Vanessa; Carvalho, Patricia Almeida; Alves, E.; Hanada, K.; Correia, J.B.Pure tungsten and tantalum plates and tungsten–tantalum composites produced via mechanical alloying and spark plasma sintering were bombarded with He+ and D+ energetic ion beams and deuterium plasmas. The aim of this experiment is to study the effects caused by individual helium and deuterium exposures and to evidence that the modifications induced in the composites at different irradiation energies could be followed by irradiating the pristine constituent elements under the same experimental conditions, which is relevant considering the development of tailored composites for fusion applications. Higher D retentions, especially in tungsten, and superficial blistering are observed in both components after helium exposure. The blistering is magnified in the tantalum phase of composites due to its higher ductility and to water vapour production under deuterium irradiation. At lower irradiation energies the induced effects are minor. After plasma exposure, the presence of tantalum does not increase the D content in the composites.
- New WC-Cu thermal barriers for fusion applications: high temperature mechanical behaviourPublication . Tejado, Elena; Dias, Marta; Correia, J.B.; Palacios, T.; Carvalho, Patricia Almeida; Alves, E.; Pastor, Jose YgnacioABSTRACT: The combination of tungsten carbide and copper as a thermal barrier could effectively reduce the thermal mismatch between tungsten and copper alloy, which are proposed as base armour and heat sink, respectively, in the divertor of future fusion reactors. Furthermore, since the optimum operating temperature windows for these divertor materials do not overlap, a compatible thermal barrier interlayer between them is required to guarantee a smooth thermal transition, which in addition may mitigate radiation damage. The aim of this work is to study the thermo-mechanical properties of WC-Cu cermets fabricated by hot pressing. Focus is placed on the temperature effect and composition dependence, as the volume fraction of copper varies from 25 to 50 and 75 vol%. To explore this behaviour, fracture experiments are performed within a temperature range from room temperature to 800 degrees C under vacuum. In addition, elastic modulus and thermal expansion coefficient are estimated from these tests. Results reveal a strong dependence of the performance on temperature and on the volume fraction of copper and, surprisingly, a slight percent of Cu (25 vol%) can effectively reduce the large difference in thermal expansion between tungsten and copper alloy, which is a critical point for in service applications. The thermal performance of these materials, together with their mechanical properties could indeed reduce the heat transfer from the PFM to the underlying element while supporting the high thermal stresses of the joint. Thus, the presence of these cermets could allow the reactor to operate above the ductile to brittle transition temperature of tungsten, without compromising the underlying materials.
- WC-Cu thermal barriers for fusion applicationsPublication . Dias, Marta; Guerreiro, F.; Tejado, Elena; Correia, J.B.; Mardolcar, U. V.; Coelho, M.; Palacios, T.; Pastor, Jose Ygnacio; Carvalho, Patricia Almeida; Alves, E.ABSTRACT: WC-Cu cermets have been devised for thermal barriers between the plasma facing tungsten tiles and the copperbased heat sink in the first wall of nuclear fusion reactors. Composite materials with 50 and 75 v/v% WC have been prepared by hot pressing at 1333 and 1423 K with pressures of 37 and 47 MPa, respectively. Microstructural changes have been investigated by scanning electron microscopy coupled with energy dispersive X-ray spectroscopy and X-ray diffraction. The materials consolidated have also been evaluated in terms of Archimedes' density, thermal diffusivity, Vickers hardness and elastic modulus. Implantation was carried out at room temperature with Ar+ at 100 keV ion beam with a fluence of 4 · 1020 at/m2. The materials consisted of homogeneous dispersions of WC particles in a Cu matrix and presented densifications of about 90%. Incipient swelling in copper-rich regions have been observed on the implanted surfaces, however no significant changes have been detected by X-ray diffraction. Higher WC content in the cermet materials increased hardness and the elastic modulus. The cermets' thermal diffusivity was significantly lower than that of pure copper or tungsten, as desirable for a thermal barrier.
- Synergistic helium and deuterium blistering in tungsten–tantalum compositesPublication . Dias, Marta; Mateus, R.; Catarino, N.; Franco, N.; Nunes, D.; Correia, J.B.; Carvalho, Patricia Almeida; Hanada, K.; Sârbu, C.; Alves, E.Tungsten–tantalum composites with 10 and 20 at.% Ta were prepared by ball milling W powder with Ta fibers and by consolidating the milled materials with spark plasma sintering. The composites were implanted at room temperature with He+ (30 keV with a fluence 5 1021 at/m2) and/or D+ (15 keV with a fluence 5 x 1021 at/m2) ion beams. The materials were studied by scanning and high-resolution transmission electron microscopy, both coupled with energy dispersive X-ray spectroscopy, and by X-ray diffraction, Rutherford backscattering spectrometry and nuclear reaction analysis. The microstructure observations revealed that the milling operation resulted in severe fragmentation of the Ta fibers. Furthermore, during the consolidation process the Ta phase acted as oxygen getter and reduced theWoxide present in the original material. The surface of the tungsten–tantalum composites implanted with D+ remained essentially unaltered, while the materials implanted with He+ evidenced blisters on the Ta-rich regions. D retention in the composites increased with He+ pre-implantation.
- New WC-Cu composites for the divertor in fusion reactorsPublication . Dias, Marta; Pinhão, N.; Faustino, R.; Martins, Ricardo; Ramos, A. S.; Vieira, M. T.; Correia, J.B.; Camacho, E.; Fernandes, F. M. Braz; Nunes, B.; Almeida, Amélia; Mardolcar, U. V.; Alves, E.ABSTRACT: The requirements for the divertor components of future fusion reactors are challenging and therefore a stimulus for the development of new materials. In this paper, WC-Cu composites are studied for use as thermal barrier between the plasma facing tungsten tiles and the copper-based heat sink of the divertor. Composite materials with 50% vol. WC were prepared by hot pressing and characterized in terms of microstructure, density, expansion coefficient, elastic modulus, Young's modulus and thermal diffusivity. The produced materials consisted of WC particles homogeneously dispersed in a Cu matrix with densifications between 88% and 98%. The sample with WC particles coated with Cu evidenced the highest densification. The thermal diffusivity was significantly lower than that of pure copper or tungsten. The sample with higher densification exhibits a low value of Young's modulus (however, it is higher compared to pure copper), and an average linear thermal expansion coefficient of 13.6 x 10(-6) degrees C-1 in a temperature range between 100 degrees C and 550 degrees C. To estimate the behaviour of this composite in actual conditions, a monoblock of the divertor in extreme conditions was modelled. The results predict that while the use of WC-Cu interlayer leads to an increase of 190 degrees C on the temperature of the upper part of the monoblock when compared to a pure Cu interlayer, the composite will improve and reduce significantly the cold-state stress between this interlayer and the tungsten.
- Effects of helium and deuterium irradiation on SPS sintered W–Ta composites at different temperaturesPublication . Mateus, R.; Dias, Marta; Lopes, J.; Rocha, J.; Catarino, N.; Franco, N.; Livramento, Vanessa; Almeida Carvalho, Patricia; Correia, J.B.; Hanada, K.; Alves, E.Energetic He+ and D+ ions were implanted into different W–Ta composites in order to investigate their stability under helium and deuterium irradiation. The results were compared with morphological and chemical modifications arising from exposure of pure W and Ta. Special attention was given to tantalum hydride (Ta2H)formation due to its implications for tritium inventory. Three W–Ta composites with 10 and 20 at.% Ta were prepared from elemental W powder and Ta fibre or powder through low-energy ball milling in argon atmosphere. Spark plasma sintering (SPS) was used as the consolidation process in the temperature range from 1473 to 1873 K. The results obtained from pure elemental samples and composites are similar. However, Ta2H is easily formed in pure Ta by using a pre-implantation stage of He+, whereas in W–Ta composites the same reaction is clearly reduced, and it can be inhibited by controlling the sintering temperature.