Electron microprobe analysis of cryolite
| Name: | Description: | Size: | Format: | |
|---|---|---|---|---|
| 1.63 MB | Adobe PDF |
Advisor(s)
Abstract(s)
A sample of cryolite was studied with a JEOL JXA 8500-F electron microprobe under several operating conditions. A TAP crystal was used to analyse Na and Al
and a LDE1 crystal to analyse F. As F and Na are both highly "volatile" elements, special care must be taken during analysis. The measurement order of Na, F
and Al is not irrelevant and optimum conditions may also result in different combinations of accelerating voltage, beam current, beam size or counting times.
Relevant X-ray signals were recorded in order to investigate the behaviour of the Na Ka and F Ka counts with elapsed time. The incident beam current was
also recorded at the same time. In a clear contrast to what has normally been reported in the EPMA analysis of aluminosilicates and silicate glasses, we found
that the Na X-ray counts increase with time. This increment of X-rays intensities for sodium in cryolite depends on the operating conditions and is
accompanied by a strong migration of fluorine from the beam excitation volume, leading to a decrease in F X-ray counting rates. It was also observed that
higher incident beam currents induce higher radiation damage in the mineral. The current instability is consistent with possible electron induced dissociation in
the cryolite structure. An analytical protocol was achieved for 6 kV and 15kV accelerating voltage for the correct EPMA analysis of cryolite.
Description
Comunicação apresentada em: EMAS 2013 : 13th European
Workshop on Modern Developments and Applications in Microbeam Analysis, Centro de Congressos da Alfândega do Porto, Portugal, 12 to 16 May 2013
Keywords
Electroquímica Geoquímica Raios X Criolite
Citation
Guimarães, F... [et al.] - Electron microprobe analysis of cryolite. In: IOP Conference Series: Materials Science and Engineering, Volume 55 (2014), conference 1